Emulsifying water and airblown asphalt with tall oil and triethandlamine

ABSTRACT

Airblown asphalt and water are hard to emulsify with either tall oil or triethanolamine as the emulsifying agent. The use of both tall oil and triethanolamine gives a synergistic effect, and weight percents based on the total weight of the emulsion of 0.9 tall oil and 0.7 triethanolamine produced stable emulsions while 1.6 of either one alone failed to produce an emulsion. Alkali metal hydroxide to adjust the pH above 7 and known emulsion stabilizing agents may be added.

United States Patent Armin C. Pitchford;

Gene N. Woodruff, both of Bartlesville, Okla.

Sept. 26, 1968 Sept. 2 l 1971 Phillips Petroleum Company Inventors Appl. No. Filed Patented Assignee EMULSIFYING WATER AND AIR-BLOWN ASPHALT WITH OIL AND TRIETHANDLAMINE 7 Claims, No Drawings U.S. Cl 252/3115, 106/277 Int. Cl B0lj 13/00 Field of Search 252/3115, 153,154, 357, 351; 106/277 To.

References Cited UNITED STATES PATENTS 5/1936 Watts 252/3115 2,256,886 9/1941 Buckley 252/31 1.5

2,679,462 5/1954 Monson.... 106/123 2,793,138 5/1957 Wilkinson 106/123 TO 2,906,633 9/1959 Thomann 106/277 OTHER REFERENCES Chemical Abstracts Vol. 42, col. 4757b, Vol. 48 col. l1069d Primary Examiner-John D. Welsh Alt0rney-Young and Quigg Emgtsu vmo WATER AND AIR-BLQWN ASPHALT wrrn OIL AND TRIETHANDLAMINE DISCLOSURE OF THE INVENTION This invention is a process of emulsifying water and airblown asphalt with a synergistic emulsifying agent comprising tall oil and triethanolamine, and a composition of matter produced thereby.

Airblown asphalt and water are hard to emulsify with either tall oil or triethanolamine as the emulsifying agent. The use of both tall oil and triethanolamine gives a synergistic effect, and weight percents based on the total weight of the emulsion of 0.9 tall oil and 0.7 triethanolamine produced stable emulsions while 1.6 of either one alone failed to produce an emulsion. Alkali metal hydroxide to adjust the pH above 7 and known emulsion stabilizing agents may be added.

In certain highly specialized applications it is often both desirable and necessary to apply high-melting asphaltic binders as coating materials at low temperatures to avoid deformation or melting of the matrix to which the asphalt is applied. This is especially true in the saturation of temperature sensitive polypropylene fabrics, such as those which are used in preparing impermeable linings for irrigation ditches, pond linings, and the like. Low temperature application is obtained by the use of an aqueous asphalt emulsion. However, this emulsification of airblown asphalts is very difficult.

In the prior art, when attempts were made to emulsify airblown asphalt and water, it has been difficult to form emulsions, even using excessively large amounts of emulsifying agents. It has now been unexpectedly discovered that when synergistic amounts of not less than 0.9 weight percent tall oil and 0.7 weight percent triethanolamine are used, a stable emulsion is formed.

In the practice of the present invention we prefer to employ Vinsol Resin (registered trademark of Hercules Powder Company), a hard, brittle, dark colored, thermoplastic resin derived from pine wood and containing phenol, aldehyde and ether groups. It has a specific gravity of 1.218, a melting point of 234-239 F., a flash point of 455 E, and an acid No. 93, largely insoluble in petroleum solvents, but soluble in alcohols, ketones and esters. It is recommended for use in slow breaking types of asphalt emulsions by Hercules Powder Company. This Vinsol Resin is a form of tall oil, and the same amount of other tall oils can be substituted with similar useful results in the practice of this invention.

Tall oil is a liquid rosin, whereas Vinsol Resin is the same material in solid form. Tall is Swedish for pine." Tall oil liquid rosin, Acintol C (trademark of Arizona Chemical Company), tallol, and talleol are all the same, being a byproduct of the wood pulp industry. Usually tall oil is recovered from pine wood black liquor" of the sulfate or kraft paper process and contains rosin acids, oleic acid and linoleic acid. Long chain alcohols and small amounts of sterols, especially phytosterol, have also been found in it. It generally is a dark brown liquid having an acrid odor similar to that of burnt rosin. Its density is 0.95 to l and its n is approximately 1.5. It has an acid No. 170-180, a saponification No. 172-185, and an iodine No. 120l88. It contains 50-60percent fatty acids, 34-40percent rosin acids, and S-lOpercent unsaponifiable material.

By tall oil we intend to cover the various tall oils, Vinsol Resin, and Acintol C.

We also employ enough alkali metal or ammonium hydroxide, preferably sodium hydroxide or potassium hydroxide, to change the acid pH caused by the Vinsol Resin to an alkaline pH above 7, preferably a pH from 10 to 12. This may be from 0.1 to 10 weight percent. Lithium, rubidium or cesium hydroxide are also operative.

We also may employ an emulsion stabilizer, but this is not essential. We can use any desired amount, such as 0.3 weight percent, of Indulin C (registered trademark of West Virginia Pulp & Paper Company), a sodium half salt of crude pine wood lignin, separated from paper pulp sulfate black liquor. It is a brown, free flowing, amorphous powder of small particle size, with a specific gravity of 1.3, a pH of 9.3, a fusion point of 200-250 C., and an apparent density of 25.9 lbs./ft.". It contains 8.3 percent moisture, 19.1 percent ash, l 1.5 percent methoxyl, and 0.8-1.5 percent sulfur. It is insoluble in dioxane and most other solvents and acids, is soluble in dilute alkaline solutions, and is dispersible in water. It is recommended for use as a stabilizer for asphalt emulsions by the West Virginia Pulp & Paper Company. However, we can make asphalt emulsions without it. They just will not be as stable. However, we can use other known emulsion stabilizers, such as 0.3 weight percent soya bean flour with equivalent results in the practice of this invention.

We also employ triethanolamine, formula (HOC H,) N, and we can use either the pure chemical or a commercial impure grade known as Polyamine T NEW made by Union Carbide.

By airblown asphalt we intend to cover all substances known to the prior art as airblown asphalt, regardless of the original grade of asphalt or details of air blowing, as all of these will operate successfully in the invention. We prepared our airblown asphalt used in table 1 below from Kansas City /200 penetration base stock by air blowing for 3.5 hours at about 460 F. with air containing about 1.6 weight percent of H PO The product had 43 penetration at 77 F. and F. ring and ball test, and was fluxed with 14 percent of the original base stock to yield a material of 47 penetration and 169 F. ring and ball test. Even if it had 49 percent unairblown and 51 percent airblown asphalt, or up to 100 percent airblown asphalt, it would be operative and would be known as airblown asphalt.

There are many patents on air blowing asphalt, some with catalysts and some without. While any airblown asphalt is satisfactory for use in the present invention, the one we prepared above is preferred, along with those prepared according to Apellaniz 2,861,940 or Hoiberg 2,450,756.

Any water, such as tap water, river water, well water or rain water, may be used.

EXAMPLE Airblown asphalt prepared as set forth above was combined with an aqueous solution of the other ingredients in a colloid mill. Any type could be used, but we used a Charlotte colloid mill. Any other type of beating the mixture can be substituted. The ingredients and amounts used in each of runs 1, 2 and 3 are shown in table 1 below. It will be noted that only in run 1 where both the Vinsol Resin and the (HOC H -,N (triethanolamine) was used was any emulsion formed. That was a stable dilatent emulsion. Dilatent means thickening upon stirring. Then the three runs were continued adding 5 weight percent water. No emulsion was formed in Runs 2 and 3, but the emulsion formed in run 1 was made nondilatent.

Table 1 shows all three runs as follows:

TABLE 1.SOLUIIONS FOR EMULSIFYING ASPHALT Second result 1 Stable dilatent emulsion.

1 N0 emulsion.

1 Stable nondilatent emulsion.

The amount of water can vary between 3 and 60 weight 7 which was Vinsol Resin, should be not less than 0.9 weight.

percent. The amount of triethanolamine, (HOC H ,N, should be not less than 0.7 weight percent. The amount of alkali metal or ammonium hydroxide should be enough to raise the pH above 7, preferably to pH l0 to 12. The amount of lndulin C or other known asphalt emulsion stabilizer, like soya bean flour, may vary from zero to about weight percent; and while emulsions can be formed without any stabilizer, it is preferred to add from 2 to 5 weight percent of any suitable emulsion stabilizer. All of the percents in this paragraph are weight percents and are based on the total weight of the emulsion produced.

When we claim an airblown asphalt aqueous emulsion consisting essentially of asphalt, water, tall oil and triethanolamine, we do not thereby exclude the other things anyone would normally add to such an emulsion if they desired, such as alkali metal hydroxide to adjust the pH, emulsion stabilizing agents such as soya bean flour, and other asphalt emulsion additives well known in the prior art and prior patents.

While a specific example has been given for illustrative purposes, the invention is not limited thereto.

We claim:

1. A process for preparing an airblown asphalt aqueous emulsion comprising the steps of combining an aqueous solution of tall oil and triethanolamine with airblown asphalt to form a mixture and agitating said mixture to thus form said emulsion wherein the total weight of said emulsion is comprised of 40 to weight percent of said airblown asphalt, at least 0.9 weight percent of said tall oil and at least 0.7 weight percent of said triethanolamine.

2. The process of claim 1 wherein there is added to said aqueous solution an alkali metal hydroxide or ammonium hydroxide in an amount such that the pH of said emulsion is above 7 3. The process of claim 2 wherein there is added to said aqueous solution a stabilizing agent selected from the group comprising Indulin C, as defined in the specification, and soya bean flour, wherein said agent is present in an amount up to 10 percent by weight of the total weight of said emulsion.

4. The product of the process of claim 1.

5. An aqueous emulsion consisting essentially of airblown asphalt, water, tall oil and triethanolamine wherein the total weight of said emulsion is comprised of 40 to 70 weight percent of said airblown asphalt, 60 to 30 weight percent of said water, at least 0.9 weight percent of said tall oil, and at least 0.7 weight percent of said triethanolamine; and further wherein said water is selected from tap water, river water, well water or rain water.

6. The emulsion of claim 5 containing in addition sufficient alkali metal hydroxide or ammonium hydroxide in an amount such that the pH of said emulsion is above 7.

7. The emulsion of claim 6 containing in addition a stabilizing agent selected from the group comprising a sodium half salt of crude pine wood lignin, and soya bean flour, wherein said agent is present in an amount up to 10 percent by weight of the total weight of said emulsion. 

2. The process of claim 1 wherein there is added to said aqueous solution an alkali metal hydroxide or ammonium hydroxide in an amount such that the pH of said emulsion is above 7 .
 3. The process of claim 2 wherein there is added to said aqueous solution a stabilizing agent selected from the group comprising Indulin C, as defined in the specification, and soya bean flour, wherein said agent is present in an amount up to 10 percent by weight of the total weight of said emulsion.
 4. The product of the process of claim
 1. 5. An aqueous emulsion consisting essentially of airblown asphalt, water, tall oil and triethanolamine wherein the total weight of said emulsion is comprised of 40 to 70 weight percent of said airblown asphalt, 60 to 30 weight percent of said water, at least 0.9 weight percent of said tall oil, and at least 0.7 weight percent of said triethanolamine; and further wherein said water is selected from tap water, river water, well water or rain water.
 6. The emulsion of claim 5 containing in addition sufficient alkali metal hydroxide or ammonium hydroxide in an amount such that the pH of said emulsion is above
 7. 7. The emulsion of claim 6 containing in addition a stabilizing agent selected from the group comprising a sodium half salt of crude pine wood lignin, and soya bean flour, wherein said agent is present in an amount up to 10 percent by weight of the total weight of said emulsion. 